What is the magnesia carbon bricks manufacturing process

magnesia carbon bricks
magnesia carbon bricks
Magnesia carbon bricks is a high melting point of basic oxide oxide (melting point 2800 ℃) and difficult to be slag invasion of high melting point carbon material as raw material, add a variety of non-oxide additives. With carbonaceous binder combination of non-burning carbon composite refractory material.


The traditional magnesia carbon brick produced by the synthetic tar binder in the cold mixing process is hardened during the damage of the tar and the necessary strength is obtained, thus forming isotropic glassy carbon. The carbon does not exhibit thermoplasticity, and the thermoplastic properties are eliminated in a large amount of stress during lining or during operation. The bituminous carbon bricks produced by the asphalt binder has a high high temperature plasticity due to the formation of anisotropic graphitized coke during the asphalt carbonization process.

Therefore, the use of asphalt combined with the brick crack resistance is higher than the asphalt bonded brick. However, one of the disadvantages of bitumen-bonded bricks is the need for thermal mixing in the production and the provision of a brick mold preheating device. In this paper, the method of making magnesia carbon brick by cold mixing process is described. The resulting bricks have a lower modulus of elasticity so that they act to eliminate stress during operation. Ordinary coal tar pitch is harmful to environmental protection due to the presence of benzophenylene. Selection of benzene and low content of the special meet the environmental requirements of the binding agent.


In order to improve its oxidation resistance, can be added in the ingredients such as Si powder, Al powder, SiC powder or ferrosilicon powder additives, resin as a binder, high pressure molding, 200 ~ 300 ℃ after treatment can be used without Calcined. Mainly used for large-scale converter and ultra-high power furnace steel lining and furnace refining furnace lining and so on.

When the carbon content is between 6% and 8%, the high temperature flexural strength, thermal shock stability, slag resistance and oxidation resistance of the magnesia carbon refractory brick are better The carbon content is low and the slag resistance of the magnesia carbon brick is reduced. When the carbon content is 14%, the oxidation resistance of the magnesia carbon brick is the worst.

More properties of magnesia carbon bricks:
http://www.ruizhirefractory.com/en/product/ladle-magnesia-carbon-brick.html
Email: sales@ruizhirefractory.com

评论

发表评论

此博客中的热门博文

Alumina magnesia carbon brick have a huge advantage in the application of steel ladle

图片
Alumina magnesia carbon brick With the development of new technologies such as refining and continuous casting, the temperature of molten steel and the residence time of molten steel in ladle can be prolonged, and the refractory material of steel ladle refractory lining is more serious. So the alumina magnesia carbon brick is developed and achieved the expected effect. Al2o3-mgo-c brick is characterized with simple construction, moderate cost, convenient unpacking and good use effect. According to the production need, ladle bricks must have good comprehensive performance.In the high alumina matrix, adding MgO powder, aluminum magnesium spinel can be formed at high temperature, improve the performance of the refractory brick . In order to improve alumina magnesia brick slag resistance, thermal shock resistance, adding the right amount of carbon materials. In order to improve the oxidation resistance of the refractory brick, adding the amount of antioxidant. Alumina magnesia carbo
阅读全文

Inspection and preparation of ladle slide gate plates

图片
ladle slide gate plates 1 Preparation of refractory mud: Phosphate mud and graphite powder in accordance with the ratio of 2: 1 poured in the mud bucket, the powder particles or debris in the group have to pick the net uniform mixing plus 20% diluted with water , Mix evenly, and covered with plastic paper to prevent dust, debris, etc. into the refractory mud. 2 Check the fire-resistant clay, skateboard brick, brick nozzle quality and site reserves, when the mud appears wet caking, skateboards and bricks do not meet the acceptance criteria prohibit the use of. 3 Check to confirm the work of two hot fix hydraulic station, working pressure should meet 12 ~ 15Mpa, cantilever crane rotation, lifting and other working conditions are normal, there are problems in time to contact the maintenance staff to deal with. 4 Check All kinds of energy medium pipeline, fittings, valves, hoses no leakage point, there is a leak must contact the handle before use. 5 All kinds of tools used in productio
阅读全文

Green mortar mass

图片
Green mortar mass Green mortar mass Introduction: Green mortar mass has good adhesion and high refractoriness, which is an ideal product to fill gaps in between slide gate plate and nozzle. The green mortar mass is to process the green mortar to the finished product as a mass, which is convenient for transportation and more convenient for customers to use. Advantage: The Green mortar mass is convenient for customers to transport and use. Green mortar mass has strong fluidity, no sintering, and no steel leakage. Green mortar mass is also commonly used in the tundish quick-change nozzle. The green mortar mass is used between the slide gate plate and the mechanism to prevent the slide gate plate from loosening steel and sticking to the machinery during use. Sourse: http://www.ruizhirefractory.com/en/product/green-mortar-mass.html Email: sales@ruizhirefractory.com
阅读全文